Standard Mid-High Fire Clays

Due to fluctuating material and shipping costs the prices on our website are not always up to date.
Please call or email us to confirm pricing prior to placing your order.

Standard Mid-High Fire Clay110050010002000
ST 101 Buff - Cone 02-9$0.63$0.57$0.50$0.45$0.41
ST 108 Red Clay w/grog ^4-10$0.77$0.69$0.61$0.54$0.49
ST 119 Stoneware$0.65$0.59$0.51$0.46$0.42
ST 153 Stoneware Cone 4-10$0.61$0.55$0.49$0.44$0.40
ST 181 White Stoneware ^6$0.79$0.72$0.63$0.56$0.51
ST 182 White Stoneware ^8$0.59$0.53$0.47$0.42$0.38
ST 182G White Stonewarew/Grog ^8$0.60$0.54$0.48$0.43$0.39
ST 205 Stoneware ^4-10$0.64$0.58$0.51$0.46$0.41
ST 257 - Grolleg Porcelain ^8-10$1.08$0.98$0.85$0.76$0.68
ST 259 Beige Stoneware ^4-10$0.60$0.54$0.47$0.42$0.38
ST 306 Brown ^4-10$0.63$0.57$0.50$0.45$0.41
ST 308 Brooklyne Red ^4-8$0.67$0.61$0.53$0.48$0.43
ST 437 Troy Porcelain$1.21$1.09$0.95$0.85$0.76
ST 507 Warm Brown Stoneware$0.67$0.61$0.54$0.48$0.44

  

C/6 Ox. C/9 Ox. C/9 R

101 BUFF CLAY (Cone 02-9)
An all purpose stoneware clay with a wide firing range for throwing and modeling.
Shrinkage: 9.5% at C/6, 12% at C/9.
Absorption: 4.5% at C/6, 3% at C/9.

C/06 Ox. C/10 Ox. C/10 R.

108 RED CLAY WITH GROG (Cone 4-10)
A high fire clay with medium grog and sand for surface texture and minimal warping and cracking. Designed for sculpture, slab or coil building.
Shrinkage:10.5% at C/6,12% at C/10.
Absorption: 5.5% at C/6, 3% at C/10.

C/6 Ox. C/10 Ox. C/10 R.

119 STONEWARE CLAY (Cone 6-10)
Contains coarse silica sand. Good for both salt and wood firings.
Shrinkage: 10.5% at C/6, 12% at C/10.
Absorption: 3.5% at C/6, 2.5% at C/10.

C/10 Ox. C/10 R.

130 PORCELAIN CLAY (Cone 7-10)
A white firing, high temperature plastic body. Very fine white porcelain grog enhances strength and throwability.
Shrinkage: 10% at C/7, 12% at C/10.
Absorption: .75% at C/7, .5% at C/10.

C/6 Ox. C/10 Ox. C/10 R.

153 STONEWARE CLAY (Cone 6-10)
A soft warm beige in oxidation - a rich gray brown in reduction. Responds well to all techniques. Excellent for production potters and classroom use.
Shrinkage: 11.5% at C/6, 13% at C/10.
Absorption: 5% at C/6, 2% at C/10.

C/6 Ox. C/10 Ox. C/10 R.

181 WHITE STONEWARE BODY (Cone 6-10)

A very smooth white stoneware body. Contains no fire clay.
Shrinkage: 13% at C/6, 13.9% at C/10.
Absorption: 2.8% at C/6, 1.7% at C/10.

C/6 Ox. C/10 Ox. C/10 R.

182 WHITE STONEWARE BODY (Cone 6-10)
Near white plastic stoneware body. Good for use with bright glazes. Available with and without fine grog. Shrinkage: 11% at C/8, 12% at C/10.
Absorption: 3% at C/8, 2.1% at C/10.

C/6 Ox. C/10 Ox. C/10 R.

205 CLAY (Cone 6-10)
Formulated for reduction firing. Muted brick red at cone 4, stone gray at cone 10. Contains fine grog.
Shrinkage: 11% at C/6, 12.5% at C/10.
Absorption: 3.5% at C/6, 1.5% at C/10.

C/10 Ox. C/10 R.

257 ENGLISH PORCELAIN (Cone 8-10)

A porcelain body with a parian like quality. It is white, tight and translucent when thin. Contains no ball clay.
Shrinkage: 13% at C/8, 15% at C/10.
Absorption: 1% at C/8, .65% at C/10.

C/6 Ox. C/10 Ox. C/10 R.

259 STONEWARE CLAY (Cone 6-10)
Formulated to be similar to 153, but with richer color tones.
Shrinkage: 12.25% at C/6, 13% at C/10.
Absorption: 4% at C/6, .85% at C/10.

C/6 Ox. C/10 Ox. C/10 R.

306 BROWN FIRING CLAY (Cone 6-10)
Smooth throwing body. Orange-brown in reduction. Muted orange to C/4 oxidation. Gray at C/10 oxidation.
Shrinkage: 11.5% at C/6, 13% at C/10.
Absorption: 3.5% at C/6, 1% at C/10.

C/6 Ox. C/8 Ox.

308 BROOKLYN RED CLAY (Cone 4-8)
Red stoneware body with sand and grog. Oxidation firing yields brick red at cone 6 and deep warm brown at cone 8.
Shrinkage: 12% at C/4, 13% at C/8.
Absorption: 2.5% at C/4, 1.0% at C/8.
C/6 Ox.  C/10 Ox.    C/10 R.507 WARM BROWN CLAY (Cone 6-10)
Stoneware body contains sand. Rich mottled orange/brown in reduction, more subdued mottling in higher oxidation firing.
Shrinkage: 10.5% at C/6, 12% at C/10.
Absorption: 3.5% at C/6, 2.5% at C/10.

Woodfired

437 TROY PORCELAIN (Cone 9-13)

A versatile, plastic English kaolin body. It throws and takes glazes well, and can be used in reduction, wood, and salt firings. Translucent when thin; wide range of color/texture in long wood firings.
Shrinkage: 13% at Cone 10, Absorption: 0.3 % at Cone 10.
Sample was woodfired without glaze.

600 TURNER'S BEST PORCELAIN (Cone 6-9)

Tom Turner's porcelain is extremely white and very plastic. Excellent for throwing and very translucent. Contains no ball clay or inorganic plasticizers. #600 is completely vitreous at C/9.
Shrinkage: 12% at C/6, 15% at C/9.
Absorption: 1.4% at C/6